Rod electrode Superchromax R3.2x300mm

For welding different
steels and for build-up welding.
Weld deposit made of austenitic
chromium-nickel-manganese steel, small
shares of delta ferrite possible.
Zero resistant up to 850 °C. The
weld metal is highly crack-resistant,
therefore also suitable for difficult-to-weld
steels and stress-compensating
buffer layers on crack-sensitive
base materials and under
hardfacings. Maximum
operating temperature for black
-white connections +300 °C. The
weld metal is hardened by
cold working. Material - No. 1.4370
EN 1600 designation: E 18 8 Mn R 12
DIN 8556 designation: E 18 8 Mn R 23
Welding positions: PA, PB, PC, PE,
PF(old DIN 1912 w, h, s, q, ü)
Materials: Joint welding of
manganese steel (1.3401),
mixed joints between unalloyed
structural steels with corrosion-resistant
steels ("black and white -connections"),
buffer layers, steels that are difficult to weld.
Dimensions: 3.2 x 300 mm Contents of each
box: 60 pieces Weight of each
box: 1.6 kg